8% carbon fiber reinforcement increases rigidity and reduces warping for precise, load-bearing parts
ASA base material provides excellent UV and weather resistance for outdoor and enclosures applications
Professional matte finish hides layer lines for a clean, aesthetic print
High heat resistance up to 103°C enables reliable printing in direct sunlight or extreme heat
Supports high-speed printing up to 350 mm/s for efficient workflow
Summarized by Shop
Engineered for Performance
Fiberon™ ASA-CF08 combines the UV and weather resistance of ASA with 8% carbon fiber by weight, delivering high rigidity, reduced warping, and a professional matte finish.
Excellent Mechanical Strength
With a bending strength of 69.1 MPa (XY) and tensile strength of 43.5 MPa (XY), ASA-CF08 offers the reliabi
Material
ASA (Acrylonitrile Styrene Acrylate) with 8% carbon fiber
Filament Diameter
1.75 mm
Bending Strength
69.1 MPa (XY-direction)
Tensile Strength
43.5 MPa (XY-direction)
Young's Modulus
36.11–181.1 MPa
Heat Deflection Temperature (HDT)
up to 103°C at 0.45 MPa
Recommended Nozzle Temperature
260–280°C
Recommended Bed Temperature
90–100°C
Recommended Fusion Temperature
190°C
Recommended Post-Processing Temperature
180–185°C
Recommended Post-Processing Time
6 hours (VST)
Recommended Supports
Polysupport for PA12
Recommended Nozzle Size
0.4 mm
Summarized by Shop
4.8
44 ratings
5
4
3
2
1
Loving this filament. I've used about 20 spools so far and they've all come out great! Definitely needs to be printed with a 0.6mm nozzle. The 0.4mm nozzles would clog occasionally. And the filament is very stiff and brittle, so need to avoid tight bends in the PTFE tubes. But I haven't had any issues using it in my Bambu AMS 2.
P
Performance · 6 days ago
Love printing with this material!!!
Dean · 10 days ago
The Polymaker ASA-CF perfect for Sculptures!
The Polymaker ASA-CF prints well straight out of thr vacuum sealed package without needing drying. There are no stringing or bubbles and layers adhere very well using a QIDi Max 4 printer with chamber st 65 C.
A great advantage is the sculpture made with this have a heft and density that gives the sculpture much more importance than lightweight PLA. It also is very strong. I use 6mm wall thickness and 25% infill!
The sculpture even without sanding or silica blasting to get rich of layer lines, look fabulous right out of the printer!